AISI 316 und AISI 316L sind die internationalen Bezeichnungen für folgende Werkstoffgüten: 1.4401 – X5CrNiMo17-12-2 (AISI 316) 1.4404 – X2CrNiMo17-12-2 (AISI 316L) 1.4435 – X2CrNiMo18-14-3 (AISI 316L) Die …
Type 316L Stainless Steel Properties. Type 316L stainless steel density is 0.289 lb/in3 (8.0 g/cm3); melting point is 1375-1400 °C (2500-2550 °F); 0.2% yield strength is minimum 25 ksi (170 MPa) in annealed and hot finished condition, minimum 45 ksi (310 MPa) in annealed and cold finished condition; Minimum tensile strength is 70 ksi (485 …
AISI 316L es una aleación de acero inoxidable austenítico considerada una de las más duraderas del mercado en la actualidad. Además de carbono, AISI 316L (que no debe confundirse con el más común y mucho menos valioso AISI 304) contiene níquel, cromo, titanio, niobio y tántalio, elementos que le permiten mantener determinadas
The annealed plates were then cold-rolled in the same direction as the original hot-rolling one to reduce their thickness by 20 ± 2%. For the five grades, Vicker's hardness increased from 135–208 HV 30 in the annealed state to 274–282 HV 30 in the cold-rolled state. The latter hardness values are higher than the maximum value of 230 …
3、:316SS≥520MPa,≥205MPa;316L≥480MPa,≥170MPa。 316L,AISI 316L,S31603,022Cr17Ni12Mo2(),Cr、Ni、Mo,。
Chemical AnalysisIt is common practice for 316L to be dual certified as 316 and 316L. The low carbon chemistry of 316L combined with an addition of nitrogen enables 316L to meet …
The ion nitriding behavior of AISI 316L austenite stainless steel was investigated at different nitriding times (2 h, 4 h, and 9 h) and temperatures (450 °C, 500 °C, and 550 °C). The structural characterization has been assessed by several considerations which can be listed: (i) the evaluation of phase distribution through Rietveld analysis of X …
This study aims to investigate the effect of the presence of a simulated corrosive body fluid (Hank's solution) on the micro-abrasion and corrosion resistance of two borided biomedical alloys (AISI 316L stainless steel and ASTM F1537 CoCrMo alloy) when in sliding contact with a ceramic countersurface. The materials were subjected to a …
Here, pulsed plasma nitriding of AISI-316L austenite stainless steel is conducted in a narrow range of temperature 510-550 °C and simultaneous combination of expanded austenite …
Summary. AISI 316 belongs to the austenitic stainless steel class. The addition of the alloying elements brings high corrosion resistance by the formation of a protective oxide …
1.4404、1.4401,AISI 316 / L-.,,。. 316 / 316LCrNiMo,2-3。. 1.4404 / 1.4401,,,
Prismatic samples (40 × 17 × 3 mm) were prepared from an AISI 316L annealed steel bar (diameter 60 mm) by cutting and then were ground and polished up to 6-μm diamond suspension; the mean surface roughness (R a value) of the polished samples was ∼ 0.25 μm. As a consequence of the grinding and polishing procedures, a small …
The AISI 316L austenite stainless steel substrates 15 × 15 × 2 mm 3 in size were used in this experiment. The substrate surface was preliminary polished by abrasive machining using #1000 to #2500 sandpaper grit to obtain the profile roughness parameter R a of 0.12–0.14 μm matching the roughness class N 10. The surface layer was synthesized …
Heat and plastic forming processes for 1.4404, 1.4401, AISI 316/316L steel. Hot forming at 1150 - 900℃. Supersaturation at 1050 - 1100℃ with water or air cooling. In the above-mentioned grades we supply companies with: Peeled and drawn bars F316, F316L. Stainless steel and spring bands strips. Stainless steel wires on spools or in coils.
AISI 316L Propriedades (Química, Mecânica E Classificação). Blog de materiais. Gelsonluz.com. dd mmmm. aaaa. URL Agora substitua dd, mm e aaaa pelo dia, mês e ano em que você navega nesta página. Substitua também URL pelo endereço real desta página. Este formato de citação é baseado no MLA e na ABNT. Especificações …
In this work, we examined the influence of different types of selective laser melting (SLM) devices on the microstructure and the associated material properties of austenitic 316L …
The corrosion rates of AISI 316L and AISI 321H austenitic stainless steel, immersed in a stagnant isothermal mixture of 60% NaNO 3 and 40% KNO 3 molten salt at 550 °C in atmospheric air are 8.6 and 9.0 µm/yr, respectively. The corrosion mechanism was proposed by recording the weight changes of the steel coupons at different time intervals …
AISI 316L as austenitic stainless steel has frequently been used in different sectors such as the medical, nuclear, aerospace, petroleum, and marine industries [1, 2].This wide range of applications for AISI 316L is because of its high corrosion resistance, strength, and biocompatibility characteristics [].So far, this alloy is the most well-known …
Gegenüber 1.4401/1.4404 ehöhtem Molybdängehalt wird korrosionsbeständigkeit gegenüber halogenhaltigen Medien und nicht oxydierenden Säuren erhöht
Milton et al. studied the microstructure of DED AISI 316L and revealed that Cr and Ni equivalent contents lie in the range of 5–10% δ-ferrite . Zietala et al. also investigated DED of AISI 316L and found that intercellular δ-ferrite formed at sub-grain boundaries as a consequence of its enrichment of Cr and Mo, and depletion of Ni .
Type 316L Stainless Steel Properties. Type 316L stainless steel density is 0.289 lb/in3 (8.0 g/cm3); melting point is 1375-1400 °C (2500-2550 °F); 0.2% yield strength is minimum 25 …
This study has evaluated the effect of different levels of cold rolling (from 0 to 50%) on the microstructural, magnetic, and mechanical properties and the corrosion behavior of 316L austenitic stainless steel in NaCl (1 mol/L) + H2SO4 (0.5 mol/L) solution. Microstructural examinations using optical microscopy revealed the development of a …